High adsorption 4a desiccant 1.6mm 3.2mm pellet zeolite 4a molecular sieve for fire escape smoke hood
Chemxin Molecular Sieve type 4A is an alkali aluminosilicate; it is the sodium form of the Type A crystal structure. 4A molecular sieve has an effective pore opening of about 4 angstroms (0.4nm). 4A molecular sieve will adsorb most molecules with a kinetic diameter of less than 4 angstroms and exclude those larger. Such adsorb-able molecules include simple gas molecules such as oxygen, nitrogen, carbon dioxide and straight chain hydrocarbons. Branched chain hydrocarbons and aromatics are excluded.
Technical Parameter:
| Model | 4A | |||
| Color | Light gray | |||
| Nominal pore diameter | 4 angstroms | |||
| Shape | Sphere | Pellet | ||
| Diameter (mm) | 1.7-2.5(8*12 mesh) | 3.0-5.0(4*8 mesh) | 1.6(1/16 inch) | 3.2(1/8 inch) |
| Size ratio up to grade (%) | ≥98 | ≥98 | ≥96 | ≥96 |
| Bulk density (g/ml) | ≥0.70 | ≥0.70 | ≥0.68 | ≥0.68 |
| Wear ratio (%) | ≤0.20 | ≤0.20 | ≤0.40 | ≤0.40 |
| Crushing strength (N) | ≥35/piece | ≥85/piece | ≥30/piece | ≥70/piece |
| Static H2O adsorption (%) | ≥21.5 | ≥21.5 | ≥21.5 | ≥21.5 |
| Static methanol adsorption (‰) | ≥15 | ≥15 | ≥15 | ≥15 |
| Water content (%) | ≤1.5 | ≤1.5 | ≤1.5 | ≤1.5 |
| Typical Chemical Formula | Na2O . Al2O3 . 2SiO2 . 4.5 H2O (SiO2 : Al2O3 ≈2) | |||
| Typical Application | a) Drying and removing of CO2 from natural gas, LPG,air, inert and atmospheric gases, etc e) For fire escape smoke hood g) For filter | |||
Regeneration:
Chemxin molecular sieve Type 4A can be regenerated by either heating in the case of thermal swing processes; or by lowering the pressure in the case of pressure swing processes.
To remove moisture from a 4A molecular sieve, a temperature of 250-280°C is required. A properly regenerated molecular sieve can give moisture dew points below -60°C.
The outlet concentrations on a pressure swing process will depend on the gas present, and on the conditions of the process.
Size:
4A - Zeolite are available in beads of 1-2 mm(10x18 mesh), 2-3 mm(8x12 mesh), 2.5-5 mm(4x8 mesh) and as powder, and in pellet 1.6mm, 3.2mm.
Attention:
To avoid damp and pre-adsorption of organic before running, or must to be reactivated.
High adsorption 4a desiccant 1.6mm 3.2mm pellet zeolite 4a molecular sieve for fire escape smoke hood
Chemxin Molecular Sieve type 4A is an alkali aluminosilicate; it is the sodium form of the Type A crystal structure. 4A molecular sieve has an effective pore opening of about 4 angstroms (0.4nm). 4A molecular sieve will adsorb most molecules with a kinetic diameter of less than 4 angstroms and exclude those larger. Such adsorb-able molecules include simple gas molecules such as oxygen, nitrogen, carbon dioxide and straight chain hydrocarbons. Branched chain hydrocarbons and aromatics are excluded.
Technical Parameter:
| Model | 4A | |||
| Color | Light gray | |||
| Nominal pore diameter | 4 angstroms | |||
| Shape | Sphere | Pellet | ||
| Diameter (mm) | 1.7-2.5(8*12 mesh) | 3.0-5.0(4*8 mesh) | 1.6(1/16 inch) | 3.2(1/8 inch) |
| Size ratio up to grade (%) | ≥98 | ≥98 | ≥96 | ≥96 |
| Bulk density (g/ml) | ≥0.70 | ≥0.70 | ≥0.68 | ≥0.68 |
| Wear ratio (%) | ≤0.20 | ≤0.20 | ≤0.40 | ≤0.40 |
| Crushing strength (N) | ≥35/piece | ≥85/piece | ≥30/piece | ≥70/piece |
| Static H2O adsorption (%) | ≥21.5 | ≥21.5 | ≥21.5 | ≥21.5 |
| Static methanol adsorption (‰) | ≥15 | ≥15 | ≥15 | ≥15 |
| Water content (%) | ≤1.5 | ≤1.5 | ≤1.5 | ≤1.5 |
| Typical Chemical Formula | Na2O . Al2O3 . 2SiO2 . 4.5 H2O (SiO2 : Al2O3 ≈2) | |||
| Typical Application | a) Drying and removing of CO2 from natural gas, LPG,air, inert and atmospheric gases, etc e) For fire escape smoke hood g) For filter | |||
Regeneration:
Chemxin molecular sieve Type 4A can be regenerated by either heating in the case of thermal swing processes; or by lowering the pressure in the case of pressure swing processes.
To remove moisture from a 4A molecular sieve, a temperature of 250-280°C is required. A properly regenerated molecular sieve can give moisture dew points below -60°C.
The outlet concentrations on a pressure swing process will depend on the gas present, and on the conditions of the process.
Size:
4A - Zeolite are available in beads of 1-2 mm(10x18 mesh), 2-3 mm(8x12 mesh), 2.5-5 mm(4x8 mesh) and as powder, and in pellet 1.6mm, 3.2mm.
Attention:
To avoid damp and pre-adsorption of organic before running, or must to be reactivated.