high alumina ceramic balls 3mm 6mm 10mm 19mm 38mm 50mm 92% Al2O3 support media alumina ball
92% High Alumina Ceramic Ball is in chemical composition92+% alpha alumina and a maximum 2wt% SiO2. Because of its high alumina content and low silica(SiO2), it's a very excellent and ideal product for high temperature and steam applications.
The Chemxin 92 High Alumina Support Media has superior chemical resistance and very excellent thermal properties, with its high density high-temperature resistance 1550℃, also it's a good choice for heat retention or equilibration media.
Technical Parameter:
| Model | 92% High Alumina Ceramic Ball | |||
| Color | White | |||
| Shape | Ball | |||
| Typical Technical Composition | Min. % | Max. % | Usual% | |
| SiO2 | ****** | 2 | 1.5 | |
| Al2O3 | 92 | 94 | 92.5 | |
Fe2O3 | ****** | 0.3 | 0.02 | |
| TiO2 | ****** | 0.1 | 0.02 | |
| CaO | ****** | 4 | 1.5 | |
| MgO | ****** | 0.1 | 0.05 | |
| Na2O | ****** | 0.25 | 0.1 | |
| K2O | ****** | 0.2 | 0.13 | |
| Physical properties | ||||
| Index | Value | Value | ||
| Leachable Iron | ≤ 0.01% | ****** | ||
| Apparent Porosity by Weight | ≤ 7.0% | ****** | ||
| Moh's Hardness Scale | >8.0 | ****** | ||
| Water Absorption | <4.0 wt.% | ****** | ||
| Acid Resistance | >99.8% | ****** | ||
| Thermal Conductivity | 0.7-0.8 w/m2.k | ****** | ||
| Thermal Expansion @ 500 | 0.10% | ****** | ||
| Thermal Shock Stability, 500℃ then water cooling | 10 times | ****** | ||
| Max. Operating Temperature | 1550°C | 2822 | ||
| Specific Density | 3200 kg/m3 | 212 lb/ft3 | ||
| Bulk Density (Packing Density) | 1900 kg/m3 | 125 lb/ft3 | ||
| Crush Strength | ||||
| Size | Crush Strength | |||
| Nominal Size | (lbs) | (kg) | (N/pc) | |
| mm | inch | min. | min. | min. |
| 3 | 1/8" | 90 | 41 | 400 |
| 6 | 1/4" | 180 | 82 | 800 |
| 10 | 3/8" | 427 | 194 | 1900 |
| 13 | 1/2" | 1304 | 592 | 5800 |
| 16 | 5/8" | 1573 | 714 | 7000 |
| 19 | 3/4" | 2023 | 918 | 9000 |
| 25 | 1" | 2697 | 1224 | 12000 |
| 38 | 1.5" | 4046 | 1837 | 18000 |
| 50 | 2" | 4832 | 2194 | 21500 |
| Typical Application | a) It's a very excellent and ideal product for high temperature and steam applications, such as secondary reformers in ammonia processing, where leached silica will coat downstream equipment or foul the catalyst bed. b) It's suitable for applications in olefin processes, such as ethylene dryers, where there's the polymerization problem. | |||
high alumina ceramic balls 3mm 6mm 10mm 19mm 38mm 50mm 92% Al2O3 support media alumina ball
92% High Alumina Ceramic Ball is in chemical composition92+% alpha alumina and a maximum 2wt% SiO2. Because of its high alumina content and low silica(SiO2), it's a very excellent and ideal product for high temperature and steam applications.
The Chemxin 92 High Alumina Support Media has superior chemical resistance and very excellent thermal properties, with its high density high-temperature resistance 1550℃, also it's a good choice for heat retention or equilibration media.
Technical Parameter:
| Model | 92% High Alumina Ceramic Ball | |||
| Color | White | |||
| Shape | Ball | |||
| Typical Technical Composition | Min. % | Max. % | Usual% | |
| SiO2 | ****** | 2 | 1.5 | |
| Al2O3 | 92 | 94 | 92.5 | |
Fe2O3 | ****** | 0.3 | 0.02 | |
| TiO2 | ****** | 0.1 | 0.02 | |
| CaO | ****** | 4 | 1.5 | |
| MgO | ****** | 0.1 | 0.05 | |
| Na2O | ****** | 0.25 | 0.1 | |
| K2O | ****** | 0.2 | 0.13 | |
| Physical properties | ||||
| Index | Value | Value | ||
| Leachable Iron | ≤ 0.01% | ****** | ||
| Apparent Porosity by Weight | ≤ 7.0% | ****** | ||
| Moh's Hardness Scale | >8.0 | ****** | ||
| Water Absorption | <4.0 wt.% | ****** | ||
| Acid Resistance | >99.8% | ****** | ||
| Thermal Conductivity | 0.7-0.8 w/m2.k | ****** | ||
| Thermal Expansion @ 500 | 0.10% | ****** | ||
| Thermal Shock Stability, 500℃ then water cooling | 10 times | ****** | ||
| Max. Operating Temperature | 1550°C | 2822 | ||
| Specific Density | 3200 kg/m3 | 212 lb/ft3 | ||
| Bulk Density (Packing Density) | 1900 kg/m3 | 125 lb/ft3 | ||
| Crush Strength | ||||
| Size | Crush Strength | |||
| Nominal Size | (lbs) | (kg) | (N/pc) | |
| mm | inch | min. | min. | min. |
| 3 | 1/8" | 90 | 41 | 400 |
| 6 | 1/4" | 180 | 82 | 800 |
| 10 | 3/8" | 427 | 194 | 1900 |
| 13 | 1/2" | 1304 | 592 | 5800 |
| 16 | 5/8" | 1573 | 714 | 7000 |
| 19 | 3/4" | 2023 | 918 | 9000 |
| 25 | 1" | 2697 | 1224 | 12000 |
| 38 | 1.5" | 4046 | 1837 | 18000 |
| 50 | 2" | 4832 | 2194 | 21500 |
| Typical Application | a) It's a very excellent and ideal product for high temperature and steam applications, such as secondary reformers in ammonia processing, where leached silica will coat downstream equipment or foul the catalyst bed. b) It's suitable for applications in olefin processes, such as ethylene dryers, where there's the polymerization problem. | |||